ABS 0215H (Jilin Petrochemical)
ABS 0215H Jilin Petrochemical – High Impact Injection Molding Grade
| Property | Test Condition | Value | Unit | Test Standard |
|---|---|---|---|---|
| Physical Properties | ||||
| Melt Flow Rate (MFR) | 220℃, 10 kg | 18 | g/10min | ASTM D1238 |
| Density | 23℃, 50% RH | 1.08 | g/cm³ | ASTM D792 |
| Mold Shrinkage | 23℃, 50% RH | 0.5–0.8 | % | ASTM D955 |
| Mechanical Properties | ||||
| Rockwell Hardness | Scale R | 99 | — | ASTM D785 |
| Tensile Yield Strength | 50 mm/min, 3.2 mm | 42 | MPa | ASTM D638 |
| Elongation at Break | 50 mm/min, 3.2 mm | 26 | % | ASTM D638 |
| Flexural Strength | 2 mm/min, 4 mm | 75 | MPa | ISO 178 |
| Flexural Modulus | 10 mm/min, 3.2 mm | 2300 | MPa | ASTM D790 |
| Izod Notched Impact Strength | 23℃, 3.2 mm | 215.6 | J/m | ASTM D256 |
| Thermal Properties | ||||
| Heat Deflection Temperature (HDT) | 0.45 MPa, unannealed | 93 | ℃ | ISO 75 |
| Heat Deflection Temperature (HDT) | 1.8 MPa, unannealed | 83 | ℃ | ISO 75 |
| Vicat Softening Point | 50℃/hr, 50 N | 98 | ℃ | ISO 306 |
| Flammability | ||||
| Flame Rating | 1.5 mm | HB | — | UL 94 |
| Flame Rating | 3.0 mm | HB | — | UL 94 |
| Optical Properties | ||||
| Yellowness Index | — | 22.8 | — | ASTM D1925 |
| Whiteness | — | 62.2 | % | ASTM D1925 |