PA66 1300S (Asahi Kasei Leona, Unreinforced Natural)
PA66 1300S (Leona™)Asahi Kasei Japan is Injection molding grade PA66 nylon pellet. Balanced high rigidity, good toughness and high flow. Suitable for automotive parts, electrical & electronic connectors, industrial mechanical components and consumer goods. Available in North America, Africa & Middle East, Europe and Asia‑Pacific markets.
| Property | Value | Unit | Test Standard |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D792 (Dry) |
| Mold Shrinkage | 1.3‑2.0 | % | Flow Direction |
| Saturated Water Absorption | 2.5 | % | 23℃ |
| Tensile Strength (Dry) | 79 | MPa | ASTM D638 |
| Elongation at Break (Dry) | 50 | % | ASTM D638 |
| Flexural Strength (Dry) | 118 | MPa | ASTM D790 |
| Flexural Modulus (Dry) | 2800 | MPa | ASTM D790 |
| Notched Izod Impact (Dry) | 39 | J/m | ASTM D256 |
| HDT @1.8MPa | 70 | ℃ | Un‑annealed |
| HDT @0.45MPa | 230 | ℃ | Un‑annealed |
| Flammability UL94 | V‑2 | – | 0.4mm |
| CTI | 600 | V | ASTM D3638 |
| Processing Method | Injection Molding | – | – |